Synthesis of Cu core Ag shell nanoparticles using chemical reduction method

Tóm tắt

A simple chemical reduction method is used to prepare colloidal bimetallic Cu–Ag core–shell (Cu@Ag) nanoparticles. Polyvinyl pyrrolidone (PVP) was used as capping agent, and ascorbic acid (C6H8O6) and sodium borohydride (NaBH4) were used as reducing agents. The obtained Cu@Ag nanoparticles were characterized by powder x-ray diffraction (XRD), transmission electron microscopy (TEM) and UV–vis spectrophotometry. The influence of [Ag]/[Cu] molar ratios on the formation of Ag coatings on the Cu particles was investigated. From the TEM results we found that the ratio [Ag+]/[Cu2+] = 0.2 is the best for the stability of Cu@Ag nanoparticles with an average size of 22 nm. It is also found out that adding ammonium hydroxide (NH4OH) makes the obtained Cu@Ag nanoparticles more stable over time when pure deionized water is used as solvent.

Từ khoá

bimetallic, core-shell structure, Cu@Ag nanoparticles, copper, silver

Tài liệu tham khảo

Huang D, Liao F, Molesa S, Redinger D and Subramanian V 2003 J. Electrochem. Soc. 150 412
Magdassi S, Bassa A, Vinetsky Y and Kamyshny A 2003 Chem. Mater. 15 2208
Lee Y, Choi J R, Lee K J, Stott N E and Kim D 2008 Nanotechnology 19 415604
Luechinger N A, Athanassiou E K and Stark W J 2008 Nanotechnology 19 445201
Yan J, Zou G, Hu A and Zhou Y N 2011 J. Mater. Chem 21 15981
Magdassi S, Grouchko M and Kamyshny A 2010 Materials 3 4626
Kim S J, Stach E and Handwerker C A 2010 Appl. Phys. Lett. 96 144101
Grouchko M, Kamyshny A and Magdassi S 2009 J. Mater. Chem 19 3057
Chen K, Ray D, Peng Y and Hsu Y 2013 Curr. Appl. Phys. 13 1496
Zhao J, Zhang D and Zhao J 2011 J. Solid State Chem. 184 2339
Tsuji M, Hikino S, Tanabe R, Matsunaga M and Sano Y 2010 Cryst. Eng. Comm. 11 3337
Lisiecki L, Billoudet F and Pileni M P 1996 J. Phys. Chem. 100 4160
Zhang J, Liu H, Wang Z and Ming N 2007 J. Solid State Chem. 180 1291
Tsai H C, Chen Y S, Song M J, Chen G Y and Lee Y H 2013 Corrosion Sci. 74 123
Dang M C, Trinh D C, Dang T M D and Fribourg-Blanc E 2013 Int. J. Nanotechnology 10 296

Các bài trích dẫn đến

1. Jiaqi Wang, Seungha Shin, Anming Hu. Geometrical effects on sintering dynamics of Cu–Ag core–shell nanoparticles in The Journal of Physical Chemistry C (Vol. 120, No. 31, 2016)
2. Xing Yu, Junjie Li, Tielin Shi, Chaoliang Cheng, Guanglan Liao, Jinhu Fan, Tianxiang Li, Zirong Tang. A green approach of synthesizing of Cu-Ag core-shell nanoparticles and their sintering behavior for printed electronics in Journal of Alloys and Compounds (Vol. 724, 2017)
3. Marta Paszkiewicz, Anna Gołąbiewska, Łukasz Rajski, Ewelina Kowal, Agnieszka Sajdak, Adriana Zaleska-Medynska. Synthesis and characterization of monometallic (Ag, Cu) and bimetallic Ag-Cu particles for antibacterial and antifungal applications in Journal of Nanomaterials (Vol. 2016, 2016)
4. Mikiko Saito, Tomohiro Ishii, Hidemichi Fujiwara, Takayuki Homma. Effect of Poly (N-vinyl-pyrrolidone) on Electrochemical Production of Cu Nanoparticles in Journal of The Electrochemical Society (Vol. 165, No. 2, 2018)
5. Supachai Sompech, Sukhontip Thaomola, Artit Chingsungnoen, Thananchai Dasri. Theoretical calculation of optical absorption property of Cu@ Ag core–shell composite nanoparticle in Materials Research Express (Vol. 6, No. 2, 2018)
6. Yunzi Liu, Wei Zhang, Helong Yu, Zhiyuan Jing, Zhanyong Song, Sijie Wang. A concise and antioxidative method to prepare copper conductive inks in a two-phase water/xylene system for printed electronics in Chemical Physics Letters (Vol. 708, 2018)
7. 崔淑媛, 刘军, 吴伟. 金属纳米颗粒导电墨水的制备及其在印刷电子方面的应用 in 化学进展 (Vol. 27, No. 10, 2015)