Impact of physical and chemical parameters on the hydroxyapatite nanopowder synthesized by chemical precipitation method

Tóm tắt

In this paper, the synthesis of hydroxyapatite (HAp) nanopowder was studied by chemical precipitation method at different values of reaction temperature, settling time, Ca/P ratio, calcination temperature, (NH4)2HPO4 addition rate, initial concentration of Ca(NO3)2 and (NH4)2HPO4. Analysis results of properties, morphology, structure of HAp powder from infrared (IR) spectra, x-ray diffraction (XRD), energy dispersive x-ray (EDX) spectra and scanning electron microscopy (SEM) indicated that the synthesized HAp powder had cylinder crystal shape with size less than 100 nm, single-phase structure. The variation of the synthesis conditions did not affect the morphology but affected the size of HAp crystals.

Từ khoá

Chemical precipitation, nano hydroxyapatite, Ca/P ratio, diameter of crystal

Tài liệu tham khảo

[1] Cengiz B, Gokce Y, Yildiz N, Aktas Z and Calimli A 2008 Colloids. Surf. A. 322 29 Crossref
[2] Jadalannagari S, More S, Kowshik M and Ramanan S R 2011 Mater. Sci. Eng. C 31 1534 Crossref
[3] Wang P, Caihong , Gong H, Jiang X, Wang H and Li K 2010 Powder Technol. 203 315 Crossref
[4] Fathi M H, Hanifi A and Mortazavi V 2008 J. Mater. Process. Technol. 202 536 Crossref
[5] Kusrini E and Sontang M 2012 Radiat. Phys. Chem. 81 118 Crossref
[6] Haberko K, Bucko M M, Brzezinska-Miecznik J, Pyda A and Zarebski J 2006 J. Eur. Ceram. Soc. 26 537 Crossref
[7] Garcia C, Garcia C and Paucar C 2012 Inorg. Chem. Commun. 20 90 Crossref
[8] Quoc Huong D and Ngoc Bich P T 2007 Vietnam J. Chem. 45 147 (in Vietnamese)
[9] Kumar A R and Kalainathan S 2010 Physica B 405 2799 Crossref
[10] Gopi D, Indira J, Kavitha L, Sekar M and Mudali U K 2012 Spectrochim. Acta A 93 131 Crossref
[11] Wang A-J, Lu Y-P, Zhu T-F, Li S-T and Ma X-L 2009 Powder Technol. 191 1 Crossref
[12] Jarudilokkul S, Tanthapanichakoon W and Boonamnuayvittaya V 2007 Colloids. Surf. A 296 149 Crossref
[13] Nasiri-Tabrizi B, Honarmandi P, Ebrahimi-Kahrizsangi R and Honarmandi P 2009 Mater. Lett. 63 543 Crossref
[14] Zhang X and Vecchio K S 2007 J. Cryst. Growth 308 133 Crossref
[15] Mobasherpour I, Heshajin M S, Kazemzadeh A and Zakeri M 2007 J. Alloys Compounds 430 330 Crossref
[16] Gouvenia D S, Bressiani A H A and Bressiani J C 2006 Mater. Sci. Forum 530–531 593 Crossref
[17] Liu C, Huang Y, Shen W and Cui J 2001 Biomaterials 22 301 Crossref
[18] Hien V D, Quoc Huong D and Ngoc Bich P T 2007 Vietnam J. Chem. 45 21 (in Vietnamese)
[19] Swain S K, Dorozhkin S V and Sarkar D 2012 Mater. Sci. Eng. C 32 1237 Crossref
[20] Kalita S J and Verma S 2010 Mater. Sci. Eng. C 30 295 Crossref
[21] Fuentes G, Hernández Y, Campos Y, López N, Rojas M L, Peón E, Almirall A and Delgado J A 2008 Latin Am. Appl. Res. 38 105–12
[22] Watters R L 2008 Calcium Hydroxyapatite (Certificate of Analysis, Standard Reference Material 2910a) (Gaithersburg, MD: Institute of Standards and Technology, NIST Measurement Services Division National) www.nist.gov/srm