Magnetic heating characteristics of La

Tóm tắt

Magnetic inductive heating (MIH) of nanoparticles (NPs) attracts considerable research attention, first because of its application to hyperthermia in biological tissues. Most reports so far have dealt with magnetite NPs with a Curie temperature, TC, of as high as above 500 °C. In this paper, we present results of a MIH study in an ac field of frequency 219 and 236 kHz and strength of 40–100 Oe for several samples of La0.7SrxCa0.3−x MnO3 NPs of TC in the region of hyperthermia, that is some tens of degrees above human body temperature. The particle materials were fabricated by a high energy mechanical milling method combined with calcining at various temperatures in the range of 600–900 °C. The heating temperatures of the samples were observed to saturate at a field irradiating time of less than 10 min and at temperatures ranging from 40 to 75 °C depending on the strontium content, the NP concentration, c, and the field parameters. A sudden change in heating rate was clearly revealed in several heating curves for the case of low applied field and low c, which was considered to be related to the onset of a strong decrease in zero-field cooling (ZFC) magnetization of NPs. The initial temperature increase slope, dT/dt, and the saturation temperature, Ts will be analyzed as dependent on the NP concentration. Field dependences of the specific loss power will be analyzed and discussed for various concentrations, c. Evidence of fluid viscosity influence will also be noted.

Tài liệu tham khảo

Gannon C J, Patra C R, Bhattacharya R, Mukherjee P and Curley S A 2008 J. Nanobiotechnol. 6 2
Rosensweig R 2002 J. Magn. Magn. Matter. 252 370
Hergt R, Dutz S, Muller R and Zeiberger M 2006 J. Phys.: Condens. Matter 18 S2919
Andra W, d'Ambly C G, Hergt R, Hilger I and Kaiser W 1999 J. Magn. Magn. Mater. 194 197
Hiergeist R, Andra W, Busk N, Hergt R, Richter U R and Kaiser W 1999 J. Magn. Magn. Mater. 201 420
Babincova M, Leszczynska D, Sourivong P, Cicmanec P and Babinec P 2001 J. Magn. Magn. Mater. 225 109
Linh P H, Manh D H, Lam T D, Hong L V, Phuc N X, Tuan N A, Ngoc N T and Tuan V A 2011 Int. J. Nanotechnol. 8 399
Kuznetsov A A, Shlyakhtin O A, Brusentsov N A and Kuznetsov O A 2002 Eur. Cells Mater. 3 (Suppl. 2) 75
Manh D H, Phong P T, Thanh T D, Hong L V and Phuc N X 2010 J. Alloys Compd. 491 8
Vasseur S, Duguet E, Portier J, Goglio G, Mornet S, Hadova E, Knizek K, Marysko M, Veverka P and Pollert E 2006 J. Magn. Magn. Mater. 302 315
Zhang K, Holloway T, Pradhan J, Bahoura M, Bah R, Rakhimov R R, Pradhan A K, Prabakaran R and Ramesh G T 2010 J. Nanosci. Nanotechnol. 10 5520
Pollert E et al 2010 Phil. Trans. R. Soc. A 368 4389
Pollert E, Veverka P, Veverka M, Kaman O, Zaveta K, Vasseur S, Epherre R, Goglio G and Dugue E 2009 Prog. Solid State Chem. 37 1
Veverka P, Pollert E, Zaveta K, Vasseur S and Duguet E 2008 Nanotechnology 19 215705
Phuc N X, Nguyen Ha M, Manh D H, Hung L T, Tuong L T C, Hong L V and Yao Y-D 2006 J. Magn. Magn. Mater. 304 133
Ha N M, Manh D H, Hong L V and Phuc N X 2008 J. Korean Phys. Soc. 52 1447
Manh D H, Phong P T, Thanh T D, Nam D N H, Hong L V and Phuc N X 2011 J. Alloys Compd. 509 1373
Phuc N X, Tuan N A, Thuan N C, Tuan V A and Hong L V 2008 Adv. Mater. Res. 55 27
Ivanov A and Kuznetsova O B 2002 J. Magn. Magn. Mater. 252 135